Huada Chemical Group as the domestic PU resin for shoe soles professional production enterprises. Always adhere to provide customers with stable quality, quality products and constantly enrich their product lines. Customized development services can be provided according to the personalized needs of customers.

1
High Hardness Polyester
HT-5890T/F-2280
1、特性:高硬度,中低密度
Characteristic:
2、用途:立跟鞋底,高坡跟
Application:Sole for casual shoes and man shoes
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5890T 液狀或石蠟狀 600~1000 1.160~1.180 18
liquid or waxy solid
F-2280 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5890T 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2280 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/116~118 7~10 40~60 0.24~0.27 45~55 3~5
Parameter
◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃
物性值 0.50~0.65 80~90 50~58 320~400 32~37 300000次無裂口
Physical properties 300000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5885B/F-2260
1、特性:高硬度,中低密度
Characteristic:
2、用途:立跟鞋底,高坡跟
Application:Sole for casual shoes and man shoes
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5885B 液狀或石蠟狀 600~1000 1.160~1.180 18
liquid or waxy solid
F-2260 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5885B 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2260 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/135~137 6~9 30~38 0.20~0.23 45~55 3~5
Parameter
◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃
物性值 0.40~0.45 85~92 50~63 320~400 30~35 300000次無裂口
Physical properties 300000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
2
Medium Hardness Polyester
HT-5600/F-2180
特性:中高硬度,中高密度
Characteristic:Medium to high hardness and medium to high density
2、用途:皮鞋、涼鞋
Application:Sole for casual shoes and man shoes
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-5600 液狀或石蠟狀 500~900 1.160~1.180 18
liquid or waxy solid
F-2180 液狀或石蠟狀 200~600 1.190~1.210 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5600 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2180 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃)
技術參數 40~45/40~45 100/119~120 8~10 50~60 0.23~0.27 45~55
Parameter
◎催化劑SM-2的加入量為230±5g/18kg The adding content of SM-2 should be 230±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃ 
物性值 0.55~0.65 65~72 50~57 350~420 33~40 300000次無裂口
Physical properties 300000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
 These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
HT-5606/F-2180
1、特性:表面光亮,手感柔和
Characteristic:smooth surface and good handle
2、用途:皮鞋、涼鞋
Application:Sole for casual shoes and man shoes
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5606 液狀或石蠟狀 800~1200 1.120~1.200 18
liquid or waxy solid
F-2180 液狀或石蠟狀 200~600 1.190~1.210 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5606 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2180 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/99~101 7~10 50~60 0.23~0.30 45~55 3~5
Parameter
◎催化劑SM-2的加入量為240±5g/18kg The adding content of SM-2 should be 240±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃
物性值 0.55~0.65 58~65 50~57 370~450 33~40 300000次無裂口
Physical properties 300000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5608B/F-2180
1、特性:中等密度,成型性好
Characteristic: medium density and good moldability
2、用途:休閑鞋、涼鞋
Application:Sole for casual shoes and man shoes
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5608B 液狀或石蠟狀 500~900 1.160~1.180 18
liquid or waxy solid
F-2180 液狀或石蠟狀 200~600 1.190~1.210 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5608B 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2180 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/116~118 9~11 40~60 0.22~0.25 45~55 3~5
Parameter
◎催化劑SM-2的加入量為270±5g/18kg The adding content of SM-2 should be 270±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃
物性值 0.46~0.55 60~65 48~55 350~450 32~37 300000次無裂口
Physical properties 300000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5650/F-2280
1、特性:成型性好,輕便
Characteristic:
2、用途:女鞋、休閑鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-5650 液狀或石蠟狀 800~1200 1.160~1.180 18
liquid or waxy solid
F-2280 液狀或石蠟狀 200~600 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5650 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2280 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/84.5~86.5 7~10 30~40 0.22~0.26 45~55 3~5
Parameter
◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
水H2O 35±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃
物性值 0.45~0.55 58~65 45~60 370~470 30~35 300000次無裂口
Physical properties 300000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.

HT-5660/F-2280
1、特性:成型性好,輕便
Characteristic:
2、用途:沙灘鞋、休閑鞋
Application:Sole for casual shoes and man shoes
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-5660 液狀或石蠟狀 1600~2000 1.150~1.170 18
liquid or waxy solid
F-2280 液狀或石蠟狀 200~600 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5660 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2280 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/119~120 7~9 35~45 0.23~0.28 45~55 3~5
Parameter
◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
水H2O 35±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃ 
物性值 0.48~0.55 55~65 45~55 350~450 30~35 300000次無裂口
Physical properties 300000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.

HT-8807/F-2500
1、特性:表皮好,成型性好,手感好
Characteristic:
2、用途:皮鞋、涼鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-8807 液狀或石蠟狀 800~1400 1.160~1.200 18
liquid or waxy solid
F-2500 液狀或石蠟狀 200~600 1.190~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-8807 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2500 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/100~102 6~9 30~40 0.23~0.27 45~55 3~5
Parameter
◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃ 
物性值 0.45~0.55 55~65 40~55 400~480 20~25 300000次無裂口
Physical properties 300000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
3
Soft Polyester
HT-5830L/F-2580L
1、特性:低硬度,手感好,耐寒性
Characteristic:
2、用途:連幫鞋和休閑鞋底
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5830L 液狀或石蠟狀 800~1200 1.170~1.190 18
liquid or waxy solid
F-2580L 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5830L 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2580L 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/54.5~56.5 7~10 40~60 0.21~0.25 45~55 3~5
Parameter
◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality 水H2O 50±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃
物性值 0.42~0.50 30~40 30~50 500~700 15~25 40000次無裂口
Physical properties 40000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5835/F-2280
1、特性:低硬度,手感好,耐水解
Characteristic:
2、用途:連幫鞋和休閑鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-5835 液狀或石蠟狀 1000~1800 1.110~1.130 18
liquid or waxy solid
F-2280 液狀或石蠟狀 200~600 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5835 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2280 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/62~64 7~10 40~60 0.21~0.25 45~55 3~5
Parameter
◎催化劑SM-2的加入量為350±5g/18kg The adding content of SM-2 should be 350±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃ 
物性值 0.42~0.50 35~40 30~45 340~400 30~35 300000次無裂口
Physical properties 300000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5840/F-2290
1、特性:低硬度,手感好
Characteristic:
2、用途:連幫鞋和休閑鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-5840 液狀或石蠟狀 1000~1800 1.170~1.190 18
liquid or waxy solid
F-2290 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5840 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2290 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/70~72 7~10 50~60 0.27~0.32 45~55 3~5
Parameter
◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at 23℃ 
物性值 0.55~0.65 35~40 25~45 340~400 30~35 300000次無裂口
Physical properties 300000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5640/F-2680
1、特性:低硬度,手感好
Characteristic:
2、用途:連幫鞋和休閑鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-5640 液狀或石蠟狀 800~1600 1.140~1.160 18
liquid or waxy solid
F-2680 液狀或石蠟狀 200~600 1.170~1.190 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5640 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2680 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/81~83 6~10 35~50 0.22~0.30 45~55 3~5
Parameter
◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality    水H2O 50±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃ 
物性值 0.40~0.55 35~40 30~40 350~400 25~30 50000次無裂口
Physical properties 50000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-6730/F-2180
1、特性:手感柔軟,成型性好
Characteristic:
2、用途:鞋墊
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-6730 液狀或石蠟狀 800~1600 1.080~1.160 18
liquid or waxy solid
F-2180 液狀或石蠟狀 200~500 1.190~1.210 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-6730 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2180 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/70~72 6~9 45~55 0.13~0.16 45~55 5~7
Parameter
◎催化劑的加入量為260±5g/18kg 
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality    
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度
Items Molded density (g/cm3) Hardness (Shore C) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm)
物性值 0.25~0.35 25~40 15~30 250~350 10~15
Physical properties
◎該物性數據是對6mm厚的試片測試獲得的數據。
 These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-6748/F-2280
1、特性:手感柔軟,撕裂性好
Characteristic:
2、用途:鞋墊、中底
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-6748 液狀或石蠟狀 700~1200 1.080~1.160 18
liquid or waxy solid
F-2280 液狀或石蠟狀 200~600 1.090~1.110 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-6748 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2280 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/73~75 6~9 45~55 0.14~0.18 45~55 5~7
Parameter
◎催化劑的加入量為250±5g/18kg 
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality    
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度
Items Molded density (g/cm3) Hardness (Shore C) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm)
物性值 0.35~0.40 50~60 14~30 250~350 20~26
Physical properties
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5335/F-2230
1、特性:手感好,低硬度,耐寒性好
Characteristic:
2、用途:耐寒鞋底、連幫鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5335 液狀或石蠟狀 600~1200 1.170~1.190 18
liquid or waxy solid
F-2230 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5335 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2230 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/60.5~62.5 7~10 50~70 0.27~0.32 45~55 3~5
Parameter
◎催化劑的加入量為450±5g/18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality    
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -15℃
物性值 0.42~0.52 30~40 30~50 500~700 15~25 40000次無裂口
Physical properties
◎該物性數據是對6mm厚的試片測試獲得的數據。
 These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-5340/F-2220
1、特性:手感好,低硬度,耐寒性好
Characteristic:
2、用途:耐寒鞋底、連幫鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-5340 液狀或石蠟狀 400~1200 1.170~1.190 18
liquid or waxy solid
F-2220 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-5340 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2220 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/63.5~65.5 7~10 50~70 0.27~0.32 45~55 3~5
Parameter
◎催化劑的加入量為360±5g/18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality    
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -25℃
物性值 0.42~0.52 30~40 30~50 500~700 15~25 40000次無裂口
Physical properties
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
4
Resin For Labor Insurance Shoe
HT-2033/F-2580
1、特性:粘結力高,手感好,耐寒性好
Characteristic:
2、用途:雙密度勞保鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-2033 液狀或石蠟狀 1400~2200 1.130~1.180 18
liquid or waxy solid
F-2580 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-2033 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2580 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 大底 中底 4~6 30~40 大底 中底 45~55 3~5
Parameter
100/63~65 100/104~106 0.55~0.7 0.22~0.26
◎催化劑SM-2的加入量為450±5g/18kg The adding content of SM-2 should be 450±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
中底:水H2O 70±5g/18kg,硬化劑800±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃ 
物性值 大底 中底 大底 中底 大底 中底 大底 中底 中底 50000次無裂口
Physical properties 0.9~1.10 0.40~0.45 66~71 45~50 50~65 35~45 550~700 400~450 20~25 50000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-8255/F-2561
1、特性:高粘結力,手感好,耐寒性好
Characteristic:
2、用途:雙密度勞保鞋和一次成型休閑鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-8255 液狀或石蠟狀 1500~2200 1.120~1.180 18
liquid or waxy solid
F-2561 液狀或石蠟狀 200~500 1.190~1.210 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-8255 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2561 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 大底 中底 6~10 50~60 大底 中底 45~55 3~5
Parameter
100/74~76 100/79~81 0.4~0.5 0.25~0.35
◎催化劑SM-2的加入量為250±5g/18kg The adding content of SM-2 should be 250±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
大底: 水H2O 20±5g/18kg
中底:水H2O 50±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -10℃ 
物性值 大底 中底 大底 中底 大底 中底 大底 中底 中底 50000次無裂口
Physical properties 0.8~1.0 0.45~0.65 55~75 40~60 >80 >45 350~450 300~400 >20 50000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-8801G/F-2580G
1、特性:高粘結力,耐寒性好,表皮光亮
Characteristic:
2、用途:耐寒勞保鞋和一次性成型休閑鞋
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cmat 40℃) Package(kg)
HT-8801G 液狀或石蠟狀 1000~1800 1.116~1.124 18
liquid or waxy solid
F-2580G 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-8801G F-2580G
60-70℃預熱6~8h 60-70℃預熱8~12h
Preheated at 60-70℃ for 6~8h Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 大底 中底 6~10 35~50 大底 中底 45~55 3~5
Parameter
100/74~76 100/81~83 0.45~0.55 0.23~0.33
◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
大底: 水H2O 20±5g/18kg
中底:水H2O 80±5g/18kg
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2 Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃ 
物性值 大底 中底 大底 中底 大底 中底 大底 中底 中底 50000次無裂口
Physical properties 0.8~1.0 0.45~0.65 60~75 50~65 76~85 42~51 380~460 300~400 30~35 50000 times no crack 
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
5
Coldtolerant Polyester
HT-2004/F-2580
1、特性:中硬度,手感好,耐寒性好
Characteristic:
2、用途:耐寒鞋底
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-2004 液狀或石蠟狀 2000~2800 1.150~1.170 18
liquid or waxy solid
F-2580 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-2004 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2580 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/94~95 7~10 50~60 0.27~0.31 45~55 3~5
Parameter
◎催化劑SM-2的加入量為220±5g/18kg The adding content of SM-2 should be 220±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -20℃
物性值 0.60~0.65 57~62 38~45 460~530 33~38 50000次無裂口
Physical properties 50000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
6
Transparent Material
HT-2005/F-2580
1、特性:中硬度,透明料
Characteristic:
2、用途:透明鞋底
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-2005 液狀或石蠟狀 1000~1600 1.150~1.170 18
liquid or waxy solid
F-2580 液狀或石蠟狀 300~700 1.180~1.200 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-2005 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-2580 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/76~78     0.9~1.2 45~55 5~7
Parameter
◎催化劑SM-2的加入量為300±5g/18kg The adding content of SM-2 should be 300±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -10℃
物性值 0.90~1.2 57~65 80~90 550~700 55~70 50000次無裂口
Physical properties 50000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
7
Polyether
HT-4460/F-4200
1、特性:耐候性優良,低溫柔順性好
Characteristic:
2、用途:大底
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-4460 液狀或石蠟狀 300~700 1.000~1.040 18
liquid or waxy solid
F-4200 液狀或石蠟狀 200~600 1.001~1.005 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-4460 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-4200 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/65~67 7~10 35~50 0.30~0.35 45~55 3~5
Parameter
◎催化劑的加入量為400±5g/18kg The adding content of SM-2 should be 400±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -40℃
物性值 0.60~0.70 55~65 45~55 450~550 15~20 50000次無裂口
Physical properties 50000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.
HT-4465/F-4230
1、特性:低溫柔順性好,防滑
Characteristic:
2、用途:大底
Application:
3、原液特性 Typical properties of PU matrix
品名 外觀 粘度 密度 包裝
Name of products Apperance Viscosity (cps at 40℃) Density (g/cm3 at 40℃) Package(kg)
HT-4465 液狀或石蠟狀 300~700 1.000~1.040 18
liquid or waxy solid
F-4230 液狀或石蠟狀 200~600 1.001~1.005 20
liquid or waxy solid
◎物料理想儲藏溫度:25℃以下
4、物料預熱 Materials preheat
HT-4465 60-70℃預熱6~8h
Preheated at 60-70℃ for 6~8h
F-4230 60-70℃預熱8~12h
Preheated at 60-70℃ for 8~12h
5、成型條件及反應參數 Typical processing parameters &Reaction parameter
項目 物料溫度 混合比 乳化時間 起發時間 泡沫密度 模具溫度 脫模時間
Items HT/F Materials temperature(℃) Mixing ratio (HT+SM)/F(By weight) Cream time(s) Rise time(s) Free foam density (g/cm3) Mold temperature(℃) Demolding time( min)
技術參數 40~45/40~45 100/53~55 7~10 40~50 0.70~0.75 45~55 3~5
Parameter
◎催化劑的加入量為340±5g/18kg The adding content of SM-2 should be 340±5g / 18kg
◎水和硬化劑根據實際需要添加   The adding content of water and hardener should added to the reality
6、制品性能 Physical properties
項目 成型密度 硬度 拉伸強度 伸長率 撕裂強度 耐折試驗
Items Molded density (g/cm3) Hardness (Shore A) Tensile strength (kg/cm2) Elongation(%)  Tear strength  (kg/cm) Flexing Endurance Test at -40℃
             
物性值 0.80~1.10 60~65 30~35 350~400 12~16 50000次無裂口
Physical properties 50000 times no crack
◎該物性數據是對6mm厚的試片測試獲得的數據。
  These physical data are acquired by testing a sample of 6mm thick.
◎自由泡沫密度會依季節(溫度、濕度)不同而變化。
  Free rise density may vary with temperature &humidity.
◎脫模時間會隨成品厚度的增加而延長。
 Demold time may be prolonged with the increase of sold thickness.  
◎以上數據及作參考,具體數據以實際操作為準,如需其它物性指標,請與我公司聯系。
 Data listed are just for reference。The detail data are subject to operation.If other request on physical properties,please contact us.